Estudio de las propiedades físico mecánicas de la fibra de coco como refuerzo de Material Compuesto Matriz Polimérica (MCMP)

Vista sencilla de ítem
dc.contributor.advisorAlvarez García, Emilio Augusto
dc.contributor.advisorMachado Rodríguez, Ángel Silvio
dc.contributor.authorMenéndez Fernández, Beatriz
dc.coverage.spatial1016432en_US
dc.date.accessioned2015-11-09T20:34:05Z
dc.date.available2015-11-09T20:34:05Z
dc.date.issued2009-07-20
dc.description.abstractEn el presente se realiza la caracterización de la fibra de coco en base al comportamiento de sus propiedades físico mecánicas para su utilización como refuerzo de material compuesto matriz polimérica. Se establece una comparación entre las fibras obtenidas en la zona cocotera de Santo Domingo y de Cayo las Vacas. A partir de los resultados del comportamiento de la fibra de coco introduce la misma en la resina de poliéster y se realizan ensayos a las muestras para determinar propiedades tales como la resistencia a la tracción, el modulo de elasticidad y el coeficiente de poisson. Como resultados fundamentales se tiene que la resistencia a la tracción de la fibra de coco de Cayo las Vacas varía entre 21 y 23MPa al igual que en Santo Domingo, el por ciento de humedad se encuentra en el rango de 0 a 10 en Santo Domingo y de 0 a 0.25 en Cayo las Vacas. El espesor oscila entre 2 a 5 mm en ambos lugares. Al añadir los diferentes tipos de fibras en la resina de poliester se tiene que para el caso de la fibra de coco las propiedades estudiadas varían en el rango de los 270 MPa para el vidrio en forma de robing 800, 131MPa para forma mat 600, en el coco es de 32MPa. Con el modulo de elasticidad el coco tiene como media 570MPa mientras la fibra de vidrio varia de1903 hasta 2402 MPa en sus dos formas. Y el coeficiente de poison no varía mucho y para el coco es de 0.075 y para el vidrio 0.15.en_US
dc.description.abstractPresently he/she is carried out the characterization of the coconut fibre based on the behaviour of their properties physique mechanics for their use like reinforcement of material compound main polymeric. A comparison settles down among the fibres obtained in Sacred Domingo's area cocotte and of Key the Cows. Starting from the results of the behaviour of the coconut fibres it introduces the same one in the polyester resin and they are carried out rehearsals to the samples to determine such properties as the resistance to the traction, the one modulates of elasticity and the Poisson coefficient. As fundamental results one has that the resistance to the traction of the fibre of coconut of Key the Cows vary between 21 and 23MPa the same as in Sacred Domingo, the percent of humidity it is in the range from 0 to 10 in Sacred Domingo and of 0 at 0.25 in Key the Cows. The thickness oscillates among 2 to 5 mm in both places. When adding the different types of fibbers in the polyester resin one has that for the case of the coconut fibre the studied properties vary in the range of the 270 MPa for the glass in robing form 800, 131MPa for form mat 600, in the coconut are of 32MPa. With the I modulate of elasticity the coconut he/she has like he/she mediates 570MPa while the glass fibre varies de1903 up to 2402 MPa in its two forms. And the poison coefficient doesn't vary a lot and for the coconut it is of 0.075 and for the glass 0.15.en_US
dc.description.sponsorshipFacultad de Ingeniería Mecánica. Departamento de Ingeniería Mecánicaen_US
dc.description.statusnon-publisheden_US
dc.identifier.urihttps://dspace.uclv.edu.cu/handle/123456789/3079
dc.language.isoesen_US
dc.publisherUniversidad Central "Marta Abreu" de Las Villasen_US
dc.rightsEste documento es Propiedad Patrimonial de la Universidad Central “Marta Abreu” de Las Villas. Los usuarios podrán hacer uso de esta obra bajo la siguiente licencia: Creative Commons: Atribución-No Comercial-Compartir Igual 4.0 Licenseen_US
dc.subjectCocoen_US
dc.subjectMaterial Compuesto Matriz Poliméricaen_US
dc.subjectPropiedades Mecánicasen_US
dc.subjectSanto Domingoen_US
dc.titleEstudio de las propiedades físico mecánicas de la fibra de coco como refuerzo de Material Compuesto Matriz Polimérica (MCMP)en_US
dc.typeThesisen_US
dc.type.thesisbacheloren_US

Archivos

Bloque original
Mostrando 1 - 1 de 1
Miniatura
Nombre:
Beatriz Menéndez Fernández.pdf
Tamaño:
611.13 KB
Formato:
Adobe Portable Document Format
Descargar
Bloque de licencias
Mostrando 1 - 1 de 1
No hay miniatura disponible
Nombre:
license.txt
Tamaño:
3.33 KB
Formato:
Item-specific license agreed upon to submission
Descripción:
Descargar

Colecciones

Tesis de Pregrado - Ingeniería Mecánica